C23400
C23400 is a brass alloy specifically designed for the initial shaping into various wrought products. This alloy is associated with a moderate base cost and a somewhat higher melting temperature compared to other types of wrought brasses.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
| Cu | 81.0 | 84.0 |
| Pb | – | 0.05 |
| Fe | – | 0.05 |
| Total Others | – | 0.20 |
| Zn | Remainder | |
MECHANICAL PROPERTIES ACCORDING TO ASTM B134 (AS PER TEMPER HO2)
| Range (mm) | From | To | UTS Min (MPa) | UTS Max (MPa) | PS Min | Elongation Min (%) | Hardness Min | Hardness Max |
| Round (Dia) | 1.5 | 6 | 540 | 620 | – | – | – | – |
| Hex (A/F) | 3 | 6 | 540 | 620 | – | – | – | – |
| Square (A/F) | 3 | 6 | 540 | 620 | – | – | – |
| PHYSICAL PROPERTIES | |
| No Physical Properties for this alloy. |
| FABRICATION PROPERTIES | |
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Fair |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Good |
| Machinability Rating | 30 |