C33500
C33500 stands as the ultimate choice for machining, boasting a flawless 100% rating on the machining index. These alloys shine just as brightly in hot stamping, especially when the forged components undergo extensive post-forging machining. Ideal for applications involving minimal cold working, such as knurling, it’s the material of choice. Its remarkable ductility sets it apart, making it perfect for crafting wires, rods, and sections.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
| Cu | 62.00 | 65.00 |
| Pb | 0.25 | 0.70 |
| Fe | – | 0.15 |
| Total Others | – | 0.4 |
| Zn | Remainder | |
MECHANICAL PROPERTIES ACCORDING TO ASTM B453 (AS PER TEMPER HO2)
| Range (Inch) | From | To | UTS Min (ksi) | UTS Max (ksi) | PS Min (ksi) | Elongation Min (%) | Hardness Min (HRB) | Hardness Max (HRB) |
| Round (Dia) | 0.059 | 0.500 | 57 | 80 | 25 | 7 | 60 | 80 |
| 0.500 | 1.000 | 55 | 70 | 25 | 10 | 50 | 75 | |
| 1.000 | 2.953 | 50 | 62 | 20 | 15 | 40 | 70 | |
| Hex (A/F) | 0.118 | 0.500 | 57 | 80 | 25 | 7 | 60 | 80 |
| 0.500 | 1.000 | 55 | 70 | 25 | 10 | 50 | 75 | |
| 1.000 | 2.756 | 50 | 62 | 20 | 15 | 40 | 70 | |
| Square (A/F) | 0.118 | 0.500 | 57 | 80 | 25 | 7 | 60 | 80 |
| 0.500 | 1.000 | 55 | 70 | 25 | 10 | 50 | 75 | |
| 1.000 | 2.362 | 50 | 62 | 20 | 15 | 40 | 70 |
| Range (mm) | From | To | UTS Min (MPa) | UTS Max (MPa) | PS Min (MPa) | Elongation Min (%) | Hardness Min (HRB) | Hardness Max (HRB) |
| Round (Dia) | 1.5 | 12 | 395 | 555 | 170 | 7 | 60 | 80 |
| 12 | 25 | 380 | 485 | 170 | 10 | 50 | 75 | |
| 25 | 75 | 345 | 425 | 140 | 15 | 40 | 70 | |
| Hex (A/F) | 3 | 12 | 395 | 555 | 170 | 7 | 60 | 80 |
| 12 | 25 | 380 | 485 | 170 | 10 | 50 | 75 | |
| 25 | 70 | 345 | 425 | 140 | 15 | 40 | 70 | |
| Square (A/F) | 3 | 12 | 395 | 555 | 170 | 7 | 60 | 80 |
| 12 | 25 | 380 | 485 | 170 | 10 | 50 | 75 | |
| 25 | 60 | 345 | 425 | 140 | 15 | 40 | 70 |
| PHYSICAL PROPERTIES | |
| Melting Point – Liquidus°F | 1700 |
| Melting Point – Solidus°F | 1650 |
| Density lb/cu in. at 68°F | 0.306 |
| Specific Gravity | 8.47 |
| Electrical Conductivity % IACS at 68°F | 26 |
| Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68°F | 67 |
| Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) | 11.3 |
| Specific Heat Capacity Btu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
| FABRICATION PROPERTIES | |
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Fair |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Machinability Rating | 60 |