C68000 Brass Brazing Rods

Low-Fuming Bronze-Nickel,This braze welding rod are similar to RBCuZn-A rods but contain additions of iron and manganese which serve to increase the hardness and strength. In addition, a small amount of silicon serves to control the vaporization of the zinc, yielding the “low-fuming” property. The nickel addition assures uniform distribution of the iron in the deposit.

SPECIFICATIONS DESIGNATION
UNS C68000
ISO 24373:2008 CuZn40Ni
DIN
EN 14640:2005 CuZn40Ni

Chemical Composition:

  Cu Ni Al Fe Mn Pb Si Sn Zn Others
Min(%) 56.0 To 60.0 0.20 To 0.80 0.01 0.25 To 1.20 0.01 To 0.50 0.5 0.04 To 0.20 0.80 To 1.10 Bal 0.5
Max(%)
Physical And Mechanical Properties
Solidus Temperature 866°C (1591°F) Liquidus Temperature 882°C (1620°F)
Density 8.39 Gms/Cm3 Tensile Strength 450 N/Mm2
Elongation 25% Brinell Hardness 96HB
Sizes Available
Wire 1.0 Mm To 11 Mm Max