CW614N

CW614N, classified as Free cutting brass, represents a notably enhanced variation of 60/40 brass, showcasing outstanding free cutting characteristics. It finds application in the high-volume fabrication of brass components where achieving maximum output and extended tool longevity is essential, and where there is no subsequent need for cold forming after the machining process.

CHEMICAL COMPOSITION
ElementsMin (%)Max (%)
Cu57.0059.00
Pb2.503.50
Fe0.30
Sn0.30
Ni0.30
Al0.05
Total Others0.20
ZnRemainder
MECHANICAL PROPERTIES ACCORDING TO EN12164 (AS PER TEMPER R430)
Range (mm) From To UTS Min (N/mm²) PS Min (N/mm²) Elongation Min (%) Hardness Min Hardness Max
Round (Dia) 2 40 430 220 10
Hex (A/F) 3 35 430 220 10
Square (A/F) 3 35 430 220 10
Rectangle (Thickness) 3 40 430 220 10
PHYSICAL PROPERTIES
Melting Point – Liquidus°F 1630
Melting Point – Solidus°F 1610
Densitylb/cu in. at 68°F 0.306
Specific Gravity 8.47
Electrical Conductivity% IACS at 68°F 28
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F 71
Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) 11.6
Specific Heat CapacityBtu/ lb /°F at 68°F 0.09
Modulus of Elasticity in Tensionksi 14000
Modulus of Rigidityksi 5300
FABRICATION PROPERTIES
Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended
Spot Weld Not Recommended
Seam Weld Not Recommended
Butt Weld Fair
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Excellent
Machinability Rating 90